Overview :

Applicable industry

This product is printing water slurry, suitable for swimsuit fabric, Lycra fabric, nylon fabric, sweaters and high elastic fabric printing, mainly for the swimwear market and development.

The appearance and composition

Sticky paste, composed of polymer emulsion.

Characteristic

Good fastness, soft, not sticky, resistant to washing, rinsing, pickling, the sea does not plug version

Application of reference

Adjustable dark

Adjustable light

HY4105 suit, white mortar

30%

HY4105 suit, white mortar

70%

HY4105B swimwear transparent paste

70%

HY4105B swimwear transparent paste

30%

Paste

X%

Paste

X%

Bake for 1 minutes ( 150℃or 150℃press 10 seconds ), or natural dry 48 hours can endure high temperature of 80 ℃wash water for 5 hours. If the mortar prepress is too thick add water, do not have to stick to strengtheningpulp.

And troubleshooting:

One possibility, resulting in poor firmness:

1, wet weather, not fully dry pulp

Guide: 150 ℃oven for 1 minutes or 150 ℃press 10 seconds.

2, and more than 10% color paste

Guide: increase the weight to reduce the transparent paste paste dosage proportion ( such as: separate pure transparent tone black ).

3, no dry pulp layer to high pressure hot

Guide: the pulp layer dry naturally into 8 or more pressure hot. ( explanation: wet slurry layer begins to presseasily cause blistering, between the slurry layer and pulp layer separation )

Two, there are several reasons caused by elastic is not what?

1, and more than 10% color paste

Guide: add weight to reduce transparent paste paste dosage ratio can be.

2, the pulp layer is too thin

Guide: print once or printing paste strength slightly, the pulp layer thickness as far as possible to stay.

3, white glue and transparent paste mix proportion improper

Guide: increase the transparent paste weight can significantly improve the pulp layer elastic.

4, wove cloth itself too deep, great flexibility

Guide : first use transparent paste 2 ~ 3 times, each time to print 3 knife, and then print white mortar or other color.

5, add the catalyst weight too much

Guide: control the dosage of the catalyst is within 2%, as long as the firm degree meet the requirements will not increase the consumption of catalysts.

Three, the cause of hard or the surface is not smooth handle

1, pulp consistency is not enough

The pulp consistency is not enough to add the thickener will improve its consistency ( explanation: pulpconsistency is not easy to cloth bottom penetration, so feel becomes hard and the surface is not smooth )

2, and more than 10% color paste

Guide: add weight to reduce transparent paste paste dosage ratio, which can significantly improve the softness of the plasma layer.

Four, the sticky surface causes and prevention?

1, the pulp layer surface dry

Guide: 150 ℃oven for 1 minutes or 150 ℃press 10 seconds.

2, the above situation does not exist, the surface or the sticky what method can be solved?

Guide: add 1 ~ 2% antisticking agent can be solved. ( overload detection method: first the pulp layer is dried, and then coated with paste layer fold with 150 degree of press 10 ~ 20 seconds, remove the tore cold hot tear test, if the slurry is flawless and perfect qualified, otherwise there will be the possibility of pulp layer bonded chainbroken )

Five, covering the cause not enough:

The ratio of 1, transparent paste.

Guide: adjust the dosage ratio can be transparent paste.

2, the slurry is too thin

Guide: slurry is too thin can add thickener stirring its consistency to improve ( explanation: pulp slurry layer is too thin to print out a relatively thin, so there will be covering the insufficient situation )

Storage

At room temperature, for a period of 6 months.